PA12 LX9016

 

VESTAMID® LX9016
聚酰胺12

Evonik Degussa GmbH  
    
 Technical Data   
    

产品说明

Heat-stabilized and light-resistant polyamide 12 compound

VESTAMID LX9016 has especially been developed for the extrusion and co-extrusion of ski upper and decorative films. Decoration on the bottom side of injection molded sports shoe soles is a further application field.

Films made of VESTAMID LX9016 feature high transparency, good screen and sublimation printing, outstanding scratch resistance, and excellent impact strength at low temperatures.

The semi-crystalline compounds based on PA12 absorb only low quantities of water.

Therefore, molded parts show excellent dimensional stability, constantly high impact strength, low coefficient of friction and good chemical resistance at changing ambient humidity.

总体

 材料状态 • 已商用:当前有效   
 资料 1 •  Technical Datasheet (English)
  
 Search for UL Yellow Card •  VESTAMID®
  
 供货地区 • 北美洲 • 欧洲  
 添加剂 • 热稳定剂 • 紫外线稳定剂  
   • Low to No Water Absorption • 极佳的可印刷性 • 耐低温撞击 
 性能特点 • 半结晶 • 抗划伤性高 • 耐化学性良好 
  • 尺寸稳定性良好 • 抗撞击性,良好 • 清晰度,高 
      
   • 低摩擦系数 • 抗紫外线性能良好 • 热稳定性 
 用途 • 薄膜   
 形式 • 颗粒   
 加工方法 • 共挤出成型 • 挤出  
     
 物理性能  额定值 单位制 测试方法 
 密度  1.01g/cm³ ISO 1183 
 机械性能  额定值 单位制 测试方法 
 拉伸模量  1070MPa ISO 527-2 
 拉伸应力 (屈服)  35.0MPa ISO 527-2/50 
 拉伸应变   ISO 527-2/50 
  屈服  5.0%  
  断裂  > 200%  
 冲击性能  额定值 单位制 测试方法 
 简支梁缺口冲击强度   ISO 179/1eA 
  -30°C, 完全断裂  17kJ/m²  
  23°C, 完全断裂  33kJ/m²  
 简支梁缺口冲击强度   ISO 179/1eU 
  -30°C  无断裂  
  23°C  无断裂  
 热性能  额定值 单位制 测试方法 
 热变形温度    
  0.45 MPa, 未退火  105°C ISO 75-2/B 
  1.8 MPa, 未退火  45.0°C ISO 75-2/A 
 维卡软化温度    
  --  170°C ISO 306/A 
  --  130°C ISO 306/B 
 备注    
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。  
 2 一般属性:这些不能被视为规格。    
1 / 2     
 

 

PA12 TR90副牌料,PA12 TR90原料,PA12 TR90水口料,PA12 TR90改性料,PA12 TR90眼镜料,电话0769-87795123
版权所有:东莞市双帮塑胶原料有限公司    网址:http://www.pa12tr90.com/
粤ICP备12050428号-3