PA12 LX9102 BLACK

 

VESTAMID® LX9102 black
聚酰胺12

Evonik Degussa GmbH  
    
 Technical Data   
    

产品说明

Conductive nylon 12 for use in multilayer tubing

VESTAMID LX9102 is a specially modified conductive nylon 12 for use in conductive multilayer tubing. VESTAMID LX9102 can be used e.g. in multilayer tubing MLT 140.2 and MLT 2040.2.

Compared to common conductive resins VESTAMID LX9102 is characterised by a lower melt viscosity and thus excellent extrudability also in thin layers. Use of VESTAMID LX9102 leads to tubing with excellent quality of the inner surface.

Multilayer tubing with an innermost layer made of VESTAMID LX9102 complies with the American automotive manufactures' requirements to avoid electrostatic charging generated by fuel flow.

总体

材料状态 • 已商用:当前有效   
资料 1 •  Technical Datasheet (English)
  
Search for UL Yellow Card •  VESTAMID®
  
供货地区 • 北美洲 • 欧洲  
性能特点 • 导电性 • 可加工性,良好  
 • 低粘度 • 良好的表面光洁度  
    
用途 • 管道   
外观 • 黑色   
形式 • 颗粒   
加工方法 • 挤出   
    
物理性能  额定值 单位制 测试方法 
密度  1.12g/cm³ ISO 1183 
吸水率   ISO 62 
饱和, 23°C  1.5%  
平衡, 23°C, 50% RH  0.50%  
机械性能  额定值 单位制 测试方法 
拉伸模量  640MPa ISO 527-2 
拉伸应力 (屈服)  40.0MPa ISO 527-2 
拉伸应变 (断裂)  190% ISO 527-2 
弯曲模量  560MPa ISO 178 
冲击性能  额定值 单位制 测试方法 
简支梁缺口冲击强度   ISO 179/1eA 
-30°C, 完全断裂  5.0kJ/m²  
23°C, 局部断裂  90kJ/m²  
简支梁缺口冲击强度   ISO 179/1eU 
-30°C  无断裂  
23°C  无断裂  
热性能  额定值 单位制 测试方法 
热变形温度    
0.45 MPa, 未退火  120°C ISO 75-2/B 
1.8 MPa, 未退火  55.0°C ISO 75-2/A 
电气性能  额定值 单位制 测试方法 
表面电阻率   IEC 60093 
--  1.0E+4ohm  
1.00 mm 3  < 1.0E+6ohm  
体积电阻率  1.0E+4ohm•cm IEC 60093 

 

1 / 3

 
 
 
 
 
 
VESTAMID® LX9102 black
聚酰胺12      Evonik Degussa GmbH  ides.com/prospector

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。

2 一般属性:这些不能被视为规格。

3 tubing 8 x 1mm

 