内容编辑

VESTAMID® L-GF30 black E70285
聚酰胺12

Evonik Degussa GmbH r 
    
 Technical Data   
    

产品说明

Glass fiber-reinforced, laser-weldable polyamide 12

VESTAMID L-GF30 black E70285 is a glass fiber-reinforced, heat-stabilized PA 12 compound with good IR laser transparency for injection molding. The material contains about 30% glass fibers, an ageing protective agent and processing aid for a fast and even form filling.

VESTAMID L-GF30 black E70285 is laserweldable by a diode-pumped or solid-state laser in the range of ? = 808-1064 nm. Using glass fiber reinforcement the strength and the heat deflection temperature are significantly increased.

Further advantages of VESTAMID L-GF30 black E70285 are the characteristic properties of polyamide 12 as low water absorption, good dimensional stability and almost the same properties at changing ambient humidity.

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet (English)
  
UL Yellow Card 2 •  E100211-217740
  
Search for UL Yellow Card •  VESTAMID®
  
供货地区 • 北美洲 • 欧洲  
填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量  
添加剂 • 加工助剂 • 热稳定剂  
性能特点 • Laser Weldable • 尺寸稳定性良好 • 热稳定性 
 • Low to No Water Absorption • 可加工性，良好  
    
外观 • 黑色   
形式 • 颗粒料   
加工方法 • 注射成型   
    
物理性能  额定值 单位制 测试方法 
密度  1.24g/cm³ ISO 1183 
收缩率 4   ISO 294-4 
横向流量: 80°C, 2.00 mm  0.90%  
流量: 80°C, 2.00 mm  0.30%  
机械性能  额定值 单位制 测试方法 
拉伸模量  6500MPa ISO 527-2 
拉伸应力 (屈服)  114MPa ISO 527-2 
拉伸应变   ISO 527-2 
屈服  5.0%  
断裂  6.0%  
冲击性能  额定值 单位制 测试方法 
简支梁缺口冲击强度   ISO 179/1eA 
-30°C, 完全断裂  21kJ/m²  
23°C, 完全断裂  23kJ/m²  
简支梁缺口冲击强度   ISO 179/1eU 
-30°C, 完全断裂  100kJ/m²  
23°C, 完全断裂  85kJ/m²  
热性能  额定值 单位制 测试方法 
热变形温度    
0.45 MPa, 未退火  175°C ISO 75-2/B 
1.8 MPa, 未退火  165°C ISO 75-2/A 
维卡软化温度  175°C ISO 306/A 
   ISO 306/B 
    
溶融温度（DSC）  178°C ISO 3146