VESTAMID® LX9020 natural color

Evonik Degussa GmbH  
 Technical Data   


High viscosity, plasticized, impact-modified, heat- and light-stabilized PA12 compound for extrusion

VESTAMID LX9020 is a plasticized polyamide 12 compound with heat and light stabilizers for the extrusion of flexible tubing and hoses especially for oil and petrochemical applications.

VESTAMID LX9020 is characterized by easy processing and good dimensional control during pipe extrusion, especially when processing large pipe diameters.

Properties of compounds based on polyamide 12 vary little with changing humidity due to low moisture absorption. Parts made of the described semi-crystalline material are characterized by exceptional impact strength, low coefficient of sliding friction and good chemical resistance.


 材料状态 • 已商用:当前有效   
 资料 1  •  Technical Datasheet (English)
 Search for UL Yellow Card •  VESTAMID®
 供货地区 • 北美洲 • 欧洲  
 添加剂  • 冲击调节器 • 增塑剂  
   • 热稳定剂 • 紫外线稳定剂  
   • Low to No Water Absorption • 经增塑 • 良好的柔韧性 
 性能特点 • 半结晶 • 抗撞击性,高 • 耐化学性良好 
  • 尺寸稳定性良好 • 抗紫外线性能良好 • 热稳定性 
   • 低摩擦系数 • 可加工性,良好 • 粘度,高 
 用途  • Oil/Gas Applications • 管道 • 管道 
 外观  • 自然色   
 形式  • 颗粒料   
 加工方法 • 挤出   
 物理性能   额定值单位制 测试方法 
 密度   1.02g/cm³ ISO 1183 
 机械性能   额定值单位制 测试方法 
 拉伸模量  380MPa ISO 527-2 
 拉伸应力   ISO 527-2 
 屈服 3  26.0MPa  
 断裂   38.0MPa  
 拉伸应变   ISO 527-2 
 屈服 3  35%  
 断裂 3  > 200%  
 断裂   > 150%  
 冲击性能   额定值单位制 测试方法 
 简支梁缺口冲击强度   ISO 179/1eA 
 -30°C, 完全断裂  7.0kJ/m²  
 23°C, 局部断裂  130kJ/m²  
 简支梁缺口冲击强度   ISO 179/1eU 
 -30°C  无断裂  
 23°C  无断裂  
 热性能   额定值单位制 测试方法 
 熔融温度 4  172°C ISO 11357-3 
 挤出   额定值单位制  
 熔体温度  230 到 250°C  
VESTAMID® LX9020 natural color
聚酰胺12      Evonik Degussa GmbH

1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。

2 一般属性:这些不能被视为规格。

3 pipe test specimens

4 2nd Heating