Evonik Degussa GmbH  
 Technical Data   


Medium-viscosity, easy mold release and heat- stabilized PA 12 compound for efficient production of injection molded parts VESTAMID X7373 is an easy mold release and heat stabilized compound.

Due to its highly effective mold release agents, VESTAMID X7373 is suitable for the efficient production of injection molded parts with very short cycle times.

VESTAMID X7373 is additionally nucleated to reduce the cycle time even further and/or to reduce the shrinkage. Properties of compounds based on polyamide 12 vary little with changing humidity due to their low moisture absorption.

Parts made of this semi-crystalline material are characterized by exceptional impact strength, low coefficient of friction and good chemical resistance.


材料状态 • 已商用:当前有效   
资料 1 •  Technical Datasheet (English)
Search for UL Yellow Card •  VESTAMID®
供货地区 • 北美洲 • 欧洲  
添加剂 • 成核剂 • 热稳定剂 • 脱模 
 • 半结晶 • 热稳定性 • 吸潮性差 
 • 低摩擦系数 • 生产阶段,快  
性能特点   • 有核 
 • 抗撞击性,良好 • 收缩性低  
   • 中等粘性 
 • 耐化学性良好 • 脱模性能良好  
形式 • 颗粒料   
加工方法 • 注射成型   

 物理性能 额定值单位制 测试方法
 密度 1.01g/cm³ ISO 1183
 收缩率 3  ISO 294-4
 横向流量: 80°C, 2.00 mm 1.2% 
 流量: 80°C, 2.00 mm 0.95% 
 吸水率  ISO 62
 饱和, 23°C 1.5% 
 平衡, 23°C, 50% RH 0.70% 
 机械性能 额定值单位制 测试方法
 拉伸模量 1500MPa ISO 527-2
 拉伸应力 (屈服) 47.0MPa ISO 527-2
 拉伸应变  ISO 527-2
 屈服 5.0% 
 断裂 > 50% 
 冲击性能 额定值单位制 测试方法
 简支梁缺口冲击强度  ISO 179/1eA
 -30°C, 完全断裂 6.0kJ/m² 
 23°C, 完全断裂 6.0kJ/m² 
 简支梁缺口冲击强度  ISO 179/1eU
 -30°C 无断裂 
 23°C 无断裂 
 热性能 额定值单位制 测试方法
 0.45 MPa, 未退火 130°C ISO 75-2/B
 1.8 MPa, 未退火 50.0°C ISO 75-2/A
1 / 3  
Evonik Degussa GmbH   
  热性能 额定值单位制 测试方法 
-- 175°C ISO 306/A 
-- 150°C ISO 306/B 

1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。

2 一般属性:这些不能被视为规格。

3 determined on 2 mm sheets with film gate at rim mold temperature 80°C