Pexidan® L/T-UV
高密度聚乙烯
SACO AEI Polymers
Technical Data
 
产品说明
High density moisture-curable PE compound for hot & cold water plumbing pipe. Suitable for DR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi.
 
PEXIDAN ® L/T (including L/T-UV and L/T Eclipse) is a high density PEX system consisting of a silane grafted base-compound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN ® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN ® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.
总览
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • SACO AEI Polymers
供货地区 • 北美洲 • 拉丁美洲 • 亚太地区
• 非洲和中东 • 欧洲
特性 • 高密度 • 抗氧化 • 可交联
用途 • 管道系统
机构评级 • ASTM F2023 • CSA B137.5 • NSF 61
• ASTM F876 • NSF 14
形式 • 粒子
加工方法 • 管路挤出成型 • 挤出
物理性能 额定值单位制 测试方法
密度 / 比重 3 0.946g/cm³ ASTM D792
熔流率(熔体流动速率) (190°C/2.16 kg) 0.70g/10 min ASTM D1238
交叉结合的程度 > 70% ASTM D2765
机械性能 额定值单位制 测试方法
拉伸模量 ISO 527-2
-40°C 2310MPa
0°C 1690MPa
23°C 862MPa
抗张强度 ASTM D638
屈服, 23°C 21.4MPa
屈服, 82°C 11.2MPa
屈服, 93°C 8.69MPa
断裂, 23°C 23.6MPa
断裂, 82°C 12.0MPa
断裂, 93°C 12.0MPa
伸长率 ASTM D638
屈服, 23°C 9.0%
屈服, 34°C 14%
屈服, 82°C 12%
断裂, 23°C 240%
断裂, 82°C 200%
断裂, 93°C 240%
弯曲模量 ISO 178
-40°C 517MPa
0°C 379MPa
23°C 207MPa
 
Pexidan® L/T-UV
高密度聚乙烯
 
SACO AEI Polymers
机械性能 额定值单位制 测试方法
流体静力学设计基础 - @ 68% DOC ASTM D2837
23°C 8.62MPa
82°C 5.52MPa
93°C 4.34MPa
热性能 额定值单位制 测试方法
维卡软化温度 124°C ASTM D1525
线形热膨胀系数 - 流动 (-100 到 85°C) 1.5E-4cm/cm/°C ASTM D696
比热 (23°C) 1920J/kg/°C
氧感应时间 (220°C) > 50min ASTM D3895
补充信息 额定值单位制 测试方法
Hot Elongation 4 内部方法
elongation under load : 150°C 30%
permanent elongation (set) after cooling : 150°C 0.0%
Curing can be done in the following ways:
• by immersion in hot water at 90-95°C
• by exposure to low pressure steam
 
In all cases curing time depends on pipe wall thickness, temperature, relative humidity and any packaging used. It is suggested that the catalyst and color masterbatches be dried for 4-6 hours at 60°C (150°F) in a desiccant dryer prior to usage.
 
挤出 额定值单位制
料筒 1 区温度 160 到 177°C
料筒 2 区温度 160 到 177°C
料筒 3 区温度 160 到 177°C
料筒 4 区温度 160 到 177°C
头部温度 365°F
口模温度 185°C
螺杆冷却 neutral
 
 
 
 
NSF饮用水处理HDPE高密度聚乙烯,NSF饮用水处理HDPE,HDPE Pexidan® L/T-UV塑料是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告,ROHS报告,REACH报告  SVHC报告,COA出厂报告,提供原料注塑加工工程中可能出现的各种异常现象解决方法,塑料牌号太多,本网站没有提供的本公司也有代理,详情请咨询本公司相关业务人员0769-87795123  微信:13549213581     联系电话:13549213581肖生  
 
 
NSF饮用水原料,NSF61饮用水原料,NSF51饮用水原料,NSF14饮用水原料,NSF饮用水ABS,NSF饮用水PP,NSF饮用水TPU,NSF饮用水POM,NSF饮用水PSU,NSF饮用水TPE,NSF饮用水PVDF,NSF饮用水PEI,NSF饮用水PE,NSF61饮用水报告,NSF51饮用水报告,NSF14饮用水报告,NSF饮用水原料物性表,NSF饮用水原料UL黄卡,NSF饮用水原料MSDS报告,NSF饮用水原料SGS报告,NSF饮用水原料ROSH报告,NSF饮用水原料COA出厂报告等相关资料               
 
 
 
 
 
 
 
 
 
 

NSF饮用水原料,NSF61饮用水原料,NSF51饮用水原料,NSF14饮用水原料,NSF饮用水ABS,NSF饮用水POM,NSF饮用水PSU,NSF饮用水PVDF,NSF饮用水PEI,NSF饮用水HDPE,NSF饮用水PA12,NSF饮用水共聚多酯,电话0769-87795123
版权所有:东莞市双帮塑胶原料有限公司    网址:http://www.pa12tr90.com/
  • 粤ICP备12050428号-3

    粤公网安备 44190002001498号